Alchem EASF Low Odour Resin is a high performance, rapid curing two part chemical anchoring system based on a modified Epoxy Acrylate resin in Methacrylate monomers. Applied in one single action this hybrid resin will produce a cost effective, strong, chemical resistant fixing.
APPROVALS
- ITB AT-15-6835/2005
Effective fixing in brick, concrete & hollow wall brackets
Non-flammable
Very low odour
High chemical resistance
Suitable for close edge applications
Suitable for use in concrete, brickwork, stone & hollow structures
Suitable for fixing wall ties, starter bars, studs & large screws
Available in 300ml and 380ml
HARDENING TIME
BASE
MATERIAL
TEMPERATURE
(°C)
GEL
TIME
mins
Min.
LOADING
TIME
mins
Min.
LOADING
TIME WET
HOLES mins
25
3
30
60
15
6
35
70
5
12
50
100
-5
50
90
180
PERFORMANCE DATA AT STANDARD EMBEDMENT DEPTH
Concrete, f, ck, cube=30N/mm²(C20/25)
Stud Thread
Size (mm) (d)
Hole Diameter
in Concrete (mm) (d0)
Hole Diameter
in Fixture
(mm) (df)
Standard Embedment
in Concrete
(mm) (b0)
Recom-
mended
Torque
(Nm) (Tinst)
Recommended
Load (kN)
Characteristics
Edge Distance
Characteristic Spacing
Tension
(Nrec)
Shear
(Vrec)
Tension
(Ccr,N)
Shear
(Ccr,V)
M8
10
9
80
11
7.3
5.8
80
100
100
M10
12
11
90
22
13.0
8.9
90
130
130
M12
14
13
110
38
17.7
13.2
110
150
150
M16
18
17
125
95
27.8
23.9
130
170
170
M20
24
22
170
170
35.5
38.2
150
190
210
M24
28
26
210
260
46.0
54.7
190
240
240
M30
35
33
280
480
82.4
69.3
300
350
350
Storage
Important
Store in a dry area between 5°C and 25°C. Do not expose to direct sunlight. Storage at higher temperatures will reduce the shelf life.
The information and data given is based on our own experience, research and testing and is believed to be reliable and accurate. However, as Alchem cannot know the varied uses to which its products may be applied, or the methods of application used, no warranty as to the fitness or suitability of its products is given or implied. It is the user’s responsibility to determine suitability of use. For further information please contact our Technical Department.